Pixel-engineered electronics have growth potential


Because graphene is atomically thin and flat and dichalcogenides like molybdenum disulfide are not quite that flat, there is some incompatibility when these are grown together—but two dichalcogenides with different compositions could be compatible.

“We show that depending on the conditions, we can combine two dichalcogenides to grow either in-plane hybrid or in stacks.”

via Pixel-engineered electronics have growth potential.